Resumen Inglés
Thin and adherent coatings of molybdenum black solar selective coatings have been produced on copper substrates by immersion in solutions with di erent concentration of ammonium molybdate. The copper sheet was polished prior to immersion in the molybdate solution. XRD analyses showed that the coating consists of di erent oxides of copper and molybdenum. The maximum solar absorptance of the resulting molybdenum black coating was 0.87 for which the thermal emittance was 0.45. The best selectivity of 4.05 was obtained for a coating made in three days in an 8.0 mM solution of ammonium molybdate, for which the absorptance was 0.81 and thermal emittance, 0.2.
Palabras clave
Resumen Español
Se produjeron recubrimientos solares selectivos delgados de molibdeno negro sobre sustratos de cobre. La técnica de crecimiento empleada fue por inmersión en soluciones con diferente concentración de molibdato de amonio. Los sustratos de cobre fueron pulidos antes de introducirse en la solución con el n de garantizar la adherencia. El análisis de difracción de rayos X reveló que los recubrimientos consisten de óxidos de cobre y molibdeno. La máxima absortancia solar de los recubrimientos de molibdeno negro resultó ser de 0.87 con un valor correspondiente de 0.45 para la emitancia térmica. La mejor selectividad alcanzada fue de 4.05 para el recubrimiento depositado durante tres días en una solución 8.0 mM de molibdato de amonio, en el que la absortancia fue de 0.81 y la emitancia térmica de 0.2.
Palabras clave